Ürün Özellikleri       ÖZELLİKLER BİRİM DEĞERLER TEST STANDARTLARI TENSILE STRENGTH AT BREAK kN >1.2 EN 60794.1.E1 BREAKING TENSILE STRENGTH kN >1.5 EN 60794.1.E1 CRUSH RESISTANCE N/cm >200 EN 60794.1.E3 REPEADING BENDING RADIUS mm <20xD EN 60794.1.E6 SINGLE BENDING RADIUS mm <15xD EN 60794.1.E6 TORSION +90° C,8 possitive EN 187 000 M 508 IMPCAT kN >1 EN 187000 M 504 TEMPERATURE     EN 60794.1.E11 OUTER SHEATH       DENSITY g/cm³ >20 ASTM D 638 TENSILE STRENGTH AT BREAK N/mm² >400 ASTM D 638 ELONGATION AT BREAK % 2/10 ASTM D 1693 E.S.C.R. (%10 lgepal C-630) >500 hours 2/10 ASTM D 746 BREAKING COLD <-75°C 2.5+0.5 ASTM D 1603 CARBON BLACK RATE % <0.950 ASTM D 792 METOT A OXIGEN INDUCTION TIME 200°C >25 IEC 811.4.2 B TUBE GEL       DENSITY (25°C) g/cm³ +0.05 DIN 51 757 DROP POINT (24 HOUR) °C aooropriate IEC 811.5.1 B DRIP POINT (24 HOUR) °C >70 REA PE 39 FLASH POINT °C >230 ISO 2592 OIL SEPERATION (150°C, 24 HOUR % 0 FTM STD 791 C VOLATILITY % <2 FTM STD 791 C WATER ARMOUNT % <0.05 DIN 51 777 ACID VALUE (100°C) % (mg KOH/g) <0.01 DIN 53 402 ABRATION   posıtıve IEC 811.5.1 PENETRATION (25°C / -30°C) 1/10 mm >150 ISO 2137 OXIGEN INDUCTION TIME (180°C) minute >20 IEC 811.4.2 B 100-500V (100°) Ω x m >10 ASTM D 1169 100-500V (23°) Ω x m   ASTM D 1169 LOSE TUBE   >10,11   DENSITY g/cm³ 1.31+0.03 ISO 1183 WATER ABSORPTION (23°C) % <0.45 DIN 53 495 TENSILE STRENGTH AT BREAK N/mm² <30 ISO 527 ELONGATION AT BREAK % >50 ISO 527 E-MODULUS N/mm² >2200 ISO 527 SHORE Shore D >78 DIN 53 505 MELTING TEMPERATURE (DSC) °C >220 ISO 3146 C LIN. THERMAL EXT. COEFF. (-23<<+80°C) °K-1 x10-4 <1.3   E-GLASS YARN       DENSITY g/cm³ offered offered TENSILE STRENGTH AT BREAK % offered offered ELONGATION AT BREAK N/mm² offered offered E-MODULUS % offered offered ARMOURING       STEEL THICKNESS nm 0.155±0.015 ASTM A 623 M TENSILE STRENGTH AT BREAK N/mm² >300 ASTM E 6892 ELONGATION AT BREAK % >15 ASTM E 6892 THICKNESS OF COATING nm >0.050±0.01 ASTM A 623 M DC RESISTANCE ohm/km <40 ASTM A 6892     ''ORing Networking Fiber ürünleri Ömür Boyu Garantilidir.''